A paper recently published in the journal ACS Applied Energy Materials demonstrated the feasibility of using a simple and effective method to exfoliate waste biomass into porous carbon with different structural levels for energy storage.

Study:  Exfoliating Waste Biomass into Porous Carbon with Multi-Structural Levels for Dual Energy Storage . Image Credit: Billion Photos/Shutterstock.com

Waste biomass-derived carbon-based materials have been used extensively in lithium-ion batteries (LIBs) and supercapacitors in recent years owing to their renewability, ease of access, good mechanical performance, and abundant storage.

Hard carbon derived from biomass possesses several advantages, including low expansion rate and electrode working potential, high capacity, and good cycling stability. Several hard carbons derived from biomass, such as walnut shells and reeds, have demonstrated exceptional electrochemical performance. 

Two-dimensional (2D) porous carbon nanosheets demonstrate a higher capacity compared to graphite, a common material used in LIB anodes, due to the increased layer spacing in them that allows greater storage of lithium ions and disorganized microcrystal stacking.

For instance, graphene-like nitrogen-doped 2D carbon nanosheets synthesized after palm spathe activation by potassium hydroxide (KOH) attained 477 mA h g−1 capacity at 0.1 A g−1 and 1297 m2 g−1 specific surface area (SSA).

Among the porous carbon materials, the open three-dimensional (3D) porous structure possesses high SSA, several quadratic active sites, low impedance, and a large electrolyte/electrode contact interface, which can considerably increase the energy density. Moreover, disordered ions can efficiently travel through this structure under high loading conditions.

Inexpensive biomasses with abundant heteroatoms and natural porous structures can act as precursors for functional carbon materials. Nitrogen/oxygen (N/O) in these porous carbons can enhance the electrochemical properties by improving the conductivity of materials and Faraday reaction pseudocapacitance.

Additionally, the formation of nitrogen-carbon (N-C) bonds can increase the contact area by regulating the electron domination of carbon, which improves the wettability between the electrolyte and porous carbon nanosheet surface.

Among the pore-making reagents traditionally used in chemical methods to prepare porous carbon, potassium hydroxide is the most efficient reagent to achieve high SSAs and fabricate different pore sizes. However, KOH causes instrument damage as it is susceptible to moisture and highly corrosive in nature, which necessitated the developed KOH-free waste biomass activation strategy.

In this study, researchers proposed using a one-step carbonization activation of waste biomass/peanut oil residues with non-toxic and eco-friendly potassium carbonate (K2CO3) to fabricate 2D porous carbon nanosheets and N/O self-doping 3D cage-like porous structures.

Peanut oil residue was initially crushed into powder and then dried for 12 h at 80 oC. The treated powder was then mixed with K2CO3, and the resultant mixture was ground and transferred to a nickel crucible.

The crucible was heated up to 900, 800, and 700 oC temperatures at a 5 oC/min heating rate under a nitrogen atmosphere for two h in a tube furnace. Subsequently, deionized water and two M hydrochloric acid were used to clean the porous carbons (PKs) to obtain a neutral filtrate.

The samples were then dried for 12 h at 80 oC and designated as PK-900, PK-800, and PK-700, respectively, depending on their respective carbonization activation temperature.

Field-emission scanning electron microscopy, high-resolution transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and Raman spectroscopy were performed for the characterization of the synthesized PK samples.

Nitrogen adsorption−desorption isotherm was performed to determine the pore size and surface area of all samples. A three-electrode system consisting of a counter electrode, a reference electrode, and a working electrode was used for supercapacitor testing.

The working electrode consisted of polytetrafloroethylene (PTFE) as a binder, acetylene black as a conductive material, and an activated carbon material dissolved in ethanol at a 1:1:8 ratio. Mercury/mercury oxide and platinum sheet were used as reference and counter electrodes, respectively.

Two electrolytes, including one M tetraethylammonium tetrafluoroborate/propylene carbonate (TEMATFB/PC) and six M KOH, were used to assess the working electrode during the supercapacitor testing.

Researchers used a CHI660E electrochemical workstation to measure the galvanostatic charge−discharge (GCD) and cyclic voltammetry curves in six M KOH. They calculated the gravimetric specific capacitances of electrodes using the GCD results during the supercapacitor testing.

During the LIB testing, the working electrode contained an activated carbon material, polyvinylidene fluoride, and acetylene black dissolved in N-methylpyrrolidone at an 8:1:1 ratio.

Porous carbon structures, including N/O self-doping 3D cage-like porous structures and 2D porous carbon nanosheets, were prepared successfully using the one-step carbonization activation of waste peanut oil residues/biomass precursor with K2CO3. This method represented an effective KOH-free biomass precursor activation strategy.

The peanut oil residue exfoliation by K2CO3 was gradually enhanced, and heteroatomic N/O self-doping was maintained at a specific amount by regulating the carbonization activation temperature, which led to the formation of N/O double-doped, pore-rich, and high-SSA carbon materials.

The synthesized porous carbon materials possessed a larger SSA in the range of 1657−2920 m2g−1, a greater degree of graphitization, and a higher nitrogen doping at 1.38−4.41% and oxygen doping at 2.48−4.98%. The porous carbon maintained a high graphitization degree even when the disordered sp2-hybridized carbon increased, resulting in good conductivity.

The fabricated PK-800 sample possessed a 3D cage-like porous structure. During supercapacitor testing, the working electrode containing PK-800 as an activated carbon material achieved an exceptional area-specific capacitance of 4400 mF cm−2 at 0.5 A g−1 at high loads of 12.5 mg cm−2, which confirmed the scalability and stability of this peanut oil residue-derived carbon structure.

Moreover, the symmetric components of PK-800 showed an excellent energy density of 60.31 W h kg−1 at 372 W kg−1 in the one M TEMATFB/PC electrolyte. The 3D porous structure retained up to 95% of its capacity at high loadings when used in the three-electrode supercapacitor in a six M KOH electrolyte.

The synthesized highly graphitized 2D porous carbon nanosheets/PK-900 demonstrated a high reversible capacity of 580 mA h g−1 at 0.1 A g−1 after 200 cycles when used in LIBs as the larger layer spacing structure efficiently stored the lithium ions.

To summarize, the findings of this study demonstrated an energy-efficient, multi-purpose, and eco-friendly strategy to activate waste biomass through one-step carbonization and exploit it in a layer-by-layer manner to prepare porous carbon at several structural levels for energy storage.

Liu, Y., Liu, X., Lin, H. et al. Exfoliating Waste Biomass into Porous Carbon with Multi-Structural Levels for Dual Energy Storage. ACS Applied Energy Materials 2022. https://pubs.acs.org/doi/10.1021/acsaem.2c01517

Disclaimer: The views expressed here are those of the author expressed in their private capacity and do not necessarily represent the views of AZoM.com Limited T/A AZoNetwork the owner and operator of this website. This disclaimer forms part of the Terms and conditions of use of this website.

Samudrapom Dam is a freelance scientific and business writer based in Kolkata, India. He has been writing articles related to business and scientific topics for more than one and a half years. He has extensive experience in writing about advanced technologies, information technology, machinery, metals and metal products, clean technologies, finance and banking, automotive, household products, and the aerospace industry. He is passionate about the latest developments in advanced technologies, the ways these developments can be implemented in a real-world situation, and how these developments can positively impact common people.

Please use one of the following formats to cite this article in your essay, paper or report:

Dam, Samudrapom. (2022, October 04). Waste Biomass-Derived Carbon Materials for Energy Storage. AZoM. Retrieved on November 03, 2022 from https://www.azom.com/news.aspx?newsID=60152.

Dam, Samudrapom. "Waste Biomass-Derived Carbon Materials for Energy Storage". AZoM. 03 November 2022. <https://www.azom.com/news.aspx?newsID=60152>.

Dam, Samudrapom. "Waste Biomass-Derived Carbon Materials for Energy Storage". AZoM. https://www.azom.com/news.aspx?newsID=60152. (accessed November 03, 2022).

Dam, Samudrapom. 2022. Waste Biomass-Derived Carbon Materials for Energy Storage. AZoM, viewed 03 November 2022, https://www.azom.com/news.aspx?newsID=60152.

Do you have a review, update or anything you would like to add to this news story?

AZoM speaks with Seokheun “Sean” Choi, a Professor in the Department of Electrical & Computer Engineering at the State University of New York. His new research details the production of a prototype circuit board printed on a sheet of paper.

Dr. Anne Meyer / Dr. Alyson Santoro

In our latest interview, AZoM spoke with Dr. Anne Meyer and Dr. Alyson Santoro who are currently collaborating as part of Nereid Biomaterials. This group is creating a new biopolymer that can be broken down by bioplastic-degrading microbes in marine environments, bringing us closer to reducing the i

This interview discusses how ELTRA, as part of Verder Scientific, produces elemental analyzers for the battery component space.

The BitUVisc is a unique model of viscometer, that can manage highly viscous samples. It is designed to keep the samples warm throughout the entire process.

Discover the FieldLab analyzer, a new, battery-powered, portable oil lab by Spectro Scientific that allows for rapid oil testing in the field.

The BeVision D2 is a dynamic image analyzer that is the perfect choice for the dynamic image analysis of dry powder and granules with its particle range of 30-10,000 microns and ability to analyze 24 different parameters.

This article provides an end-of-life assessment of lithium-ion batteries, focusing on the recycling of an ever-growing amount of spent Li-Ion batteries in order to work toward a sustainable and circular approach to battery use and reuse.

Corrosion is the degradation of an alloy caused by its exposure to the environment. Corrosion deterioration of metallic alloys exposed to the atmosphere or other adverse conditions is prevented using a variety of techniques.

Due to the ever-increasing demand for energy, the demand for nuclear fuel has also increased, which has further created a significant increase in the requirement for post-irradiation examination (PIE) techniques.

AZoM.com - An AZoNetwork Site

Owned and operated by AZoNetwork, © 2000-2022